transparent biaxially oriented polypropylene cigarette film featured coextruded heat sealable on both sides,incorporated with anti- static protection
Thickness : 18,19,20,21,22,25 Microns
Width: 90,110,118,120,135,150,220,350MM   Length:2000M,2800M,3000M,3500M
 Well-fitting to machine, suitable for high speed packing of all kinds of soft pack. Special hot slip ability on surface,can avoid machine-blocking,sticking etc. Quick heat sealing at low temperature and pressare. Good foldability after forming. Inferior optical properties to others.
Customer's own requirement is available for us such as printed OEM logos and private label or particular size and package style.
b.) Half-shrinkage BOPP Cigarette Film with heat sealable matches high-speed packaging machines.

Size: 22Microns*105mm*2800M

22Microns*110mm*2800M

22Microns*115mm*2800M

22Microns*118mm*2800M

22Microns*120mm*2800M

22Microns*125mm*2800M

22Microns*130mm*2800M

22Microns*135mm*2800M

22Microns*225mm*2800M

22Microns*350mm*2800M

22Microns*380mm*2800M

22Microns*420mm*2800M

c.) High-shrinkage BOPP Cigarette Film with heat sealable matches high-speed packaging machines.

3.) Specific property

Unit Typical numerical value  Testing Standard Grade AEC21 Grade AEC22 Corporate National International
 Density g/cm3 0.905 0.905 ASTM D1505
Thickness μm 21 22 Q/SD2 GB/T6672-2001
Unit weight g/m2 19.0 19.9
Yield m2/kg 52.6 50.3
Tensile strength MD N/mm2 160 150 Q/SD2 GB/T1040-1992 ASTM D882 TD 287 280
Elongation at break MD % 172 180 Q/SD2 GB/T1040-1992 ASTM D882 TD 63 60
Heat shrinkage MD % 3.5 3.2 Q/SD2 GB/T12026-2000 ASTM D1204-89 TD 2.8 2.5
Young’s modulus MD N/mm2 2200 1980 Q/SD2 ASTM D882 TD 3900 3300
Heat sealing strength N/15mm 2.6 2.7 Q/SD2 QB/T2358-1998 ASTM F88-94
Temperature range of heat sealing °C 120~150 120~150 Q/SD2 QB/T2358-1998 ASTM F88-94
Friction co-efficient 0.20 0.20 Q/SD2 GB/T10006-1988 ASTM D1894-93
Haze % 1.3 1.5 Q/SD2 GB2410-1980 ASTM D1003-95
(45°) Gloss % 85.0 85.0 Q/SD2 GB8807-1988 ASTM D2457