two-side coated, sealable OPP film used primarily as the outside web in laminations. Are sealable to other acrylic-coated and sealable PVdC-coated films. Arcylic coating and its properties are not affected by humidity.
FILM TECHNICAL SPECS:
Properties
unit
Test method
Tolerance
Typical value
Thickness
micron
--
±3%
20
Yield
m²/ kgm
--
±3%
55
Unit weight
gm/m²
--
±3%
18.2
Tensile strength
MD
TD
N/mm²
ASTM D 882
Min.
Min.
120
240
Breaking elongation
MD
TD
%
ASTM D 882
± 20
± 10
160
50
Modulus of elasticity
MD
TD
N/mm²
ASTM D 882
Min.
Min.
2000
3400
Heat shrinkage
MD
TD
%
In air, in oven for 5 min. at 130 ºC
Max.
Max.
4
2
Haze
%
ASTM D 1003
Max.
2.5
Gloss
G.U.
ASTM D 2457
Min.
85
Coefficient of friction
--
ASTM D 1894
± 0.05
0.3
Water vapor permeability
g/m².24 hrs at 38 ºC 90% RH
ASTM E 96-66 BS 3177
Max.
8.3
Oxygen permeability
Cc/m². 24 hrs Bar, at 23º C, 0% RH
ASTM D1434 Bs 2782 – 514 A
Max.
2200
Heat Seal Ring
ºC
OPMA METHOD
--
120 -145
Density
Kgm/m³
ASTM D 1505
± 0.05
0.91
FILM DESCRIPTION:
Two sides heat sealable; one side treated co extruded biaxial oriented polypropylene transparent film, suitable for:
Rotogravure and flexographic printing.
Lamination with similar films, paper or other films.
Horizontal and vertical packaging machines (HFFS – VFFS).
General over wrapping purposes.
CHARACTERISTICS
Two sides heat sealable with excellent hot tack.
High transparency.
Excellent ink adhesion on treated side.
High resistance to oil, grease, chemicals, puncture and abrasion.
Good barrier to moisture, odors and gases.
APPLICATIONS:
Food packaging:
Biscuit, pasta, snacks, confectionary, chips, tea, and bakery.